Alteration in the Microstructure of Fly Ash Geopolymers upon Exposure to Elevated Temperatures

Abstract:

This paper represents the mechanical and microstructure changes in geopolymeric material synthesized by the alkali activation of locally source fly ash at high temperatures of 400, 600 and 800 °C. The high compressive strength of geopolymer cured at 70 °C underwent thermal shrinkage and substantial strength losing at temperatures of 400, 600 °C caused by the high dehydration of the structural water. Exposure to temperature of 800 °C, the geopolymer lost its strength due to extremely densification and expansion processes of the high unreacted silicate phase in the structure. The SEM results showed that the high activator content generated large quantities of unreacted silicate crystals at high temperatures which sintered at range of temperatures of 700-800 °C causing system failure.

• Periodical: Advanced Materials Research (Volume 795)
• Pages: 201-205
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.795.201
• Online since: September 2013
• Authors: Omar A. Abdulkareem, Mohd Mustafa Al Bakri Abdullah, H. Kamarudin, Khairul Nizar Ismail
• Keywords: Elevated Temperatures, Geopolymer, SEM, Strength Loss, Thermal Shrinkage

References

[1] J. Davidovits, Chemistry of geopolymeric systems, terminology in: proceeding of International Conference on geopolymers, Geopolymer '99 International conference, Geopolymer Institute, France. 32: 9–40 (1999).

[2] K. Yang, J. Song, and J. Lee. J Mater struct. 43(2010):403-416.

[3] Z. Li, Z. Ding and Y. Zhang, Development of sustainable cementitious materials in: International Workshop on Sustainable Development and Concrete Technology, edited by K. Wang, Beijing, China, May 20-21(2004).

[4] S. Wallah and B. Rangan, Low- calcium fly ash based geopolymer concrete: Long-term properties. Research Report GC 2, Curtin University of Technology, Perth,Australia, (2006): p.97.

[5] J. Gourley and G. Johnson, Developments in geopolymer precast concrete. In: proceeding of fourth World Congress geopolymer, Geopolymer Institute, France. (2005) 133-137.

[6] ASTM C618-08a, Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete, Annual book of ASTM standard, Philadelphia, USA, 4.02 (2008).

DOI: 10.1520/c0618-99

[7] S. Hu, J. WU, Y. Wen, Y. HE, W. Fa-Zhou and D. Qing-Jun. J Cent Sou Univer Techno. 16 (2009):914-918.

[8] W. Rickard, A. van Riessen, P. Walls, Int. J. Appl. Ceram. Technol. 7 (2010) 81–88.

[9] J. Provis, C. Yong, P. Duxson, J. van Deventer, Colloids Surf. A 336 (2009)57–63.

[10] P. Duxson, G.C. Lukey, J.S.J. van Deventer, J. Non-Cryst. Solids 352 (2006) 2186–2200.

[11] W. Rickard, J. Temuujin, A van Riessen, J. Non-Cryst. Solids 385 (2012) 1380- 1389.